产品名称

High Wear-Resistant Smooth Anode Electrophoretic Paint

The anodic electrophoretic paint is developed by our company on the basis of the original electrophoretic paint ED-6 according to the current market feedback, most of which have poor hand feeling and poor fingerprint resistance.
没有此类产品
Description
I. Introduction
 
The anodic electrophoretic paint is developed by our company on the basis of the original electrophoretic paint ED-6 according to the current market feedback, most of which have poor hand feeling and poor fingerprint resistance. Compared with the original electrophoretic paint ED-6, it not only has the original characteristics of good water solubility and high solid content. At the same time, after electrophoretic film formation, the paint film surface has better hand feeling, higher smoothness and better fingerprint resistance. In the current competitive electrophoresis industry, our company has greatly increased the market competitiveness for customers on the premise of not increasing customers' existing costs as much as possible.
 
 
II. Specifications
 

Item

Specification

Test Conditions

Appearance

Light yellow and clear

Visual inspection

Solid content

60±2%

105℃×3hrs

Viscosity

Z1～Z2

Gardner at 25℃

Pigment

＜2

Grander
 
III. Performance
 

Item

Performance

Test Conditions

Appearance

Flat and flawless

Visual inspection

Gloss (60℃)

120°

8μ, brown color

Hardness

3H～4H

Baking 180℃, 30 minutes, Mitsubishi pencil

Adhesion

100∕100

Paint adhesion testing

Alkali resistance

No abnormal

0.5%，NaOH 20 +/–1℃ 24 hours

Acid resistance

No abnormal

5% HCl 　 20 +/–1℃ 24 hours

Weather resistance

Retention rate 90%

QUV weather resistance test, 1000 hours

Boiling water resistance

No abnormal

95＜boiling water＜98℃　5 hours

Salt resistance

No abnormal

CASS  72 hours

 

At the same time, our company can provide 200KG and 50KG packing barrels according to the customer's site requirements, which is convenient for customers to store and add the paint.

Corresponding parameter set not found, please add it in property template of background
暂未实现,敬请期待
暂未实现,敬请期待
Anode low-temperature curing varnish
Next article

RECOMMEND

Traditional Varnish

Oxidation-Free Color Electrophoresis
MESSAGES

Guangzhou Youda Coating Co., Ltd.

If you are interested in our products,
Please fill in the requirements and

leave me a message!